Impact of Polyimide Film Thickness for Improving the Mechanical Robustness of Stretchable InGaZnO Thin-Film Transistors Prepared on Wavy-Dimensional Elastomer Substrates

We report on the In-Ga-Zn-O thin-film transistors (IGZO TFTs) with outstanding mechanical stretchability, which were fabricated on ultrathin polyimide (PI) film/prestrained elastomer with a wavy-dimensional structure. The device characteristics of the fabricated devices were evaluated under mechanically strained conditions with various strains. The operational reliabilities against the bias stress conditions and during the cyclic stretching tests were also carefully examined. The stretchable IGZO TFTs exhibited good device operations without any marked degradation under stretching/compressed conditions with a strain of 40%. Under positive bias stress with a prestrain of 50%, the turn-on voltage instabilities for the TFTs prepared on 0.9 and 2.0 μm-Thick PI films were estimated to be 1.5 and 3.9 V, respectively. During the cyclic stretching tests with a strain of 50%, the device operations failed after 20,000 and 100,000 stretching cycles for the TFTs fabricated on 2.0 and 0.9 μm-Thick PI films, respectively. As a result, the IGZO TFTs fabricated on a thinner PI film presented more reliable operations after the repeated stretching events. The robust mechanical stretchability dependent on the PI film thickness was suggested to be due to the difference in critical values of bending radii and the influence of the local strain induced by the spatial fluctuations of the wavy structures.