Synthesis and Eu³⁺ concentration-dependent photoluminescence of Gd_2-xEu_xO₃ nanowires

The nanowire growth behavior and photoluminescence characteristics of red-emitting oxide phosphor Gd_2-xEu_xO₃ have been investigated in the function of activator (Eu³⁺) concentrations (x=0.08, 0.12, 0.16, 0.20, and 0.24). Nanowires of Gd_2-xEu_xO₃ phosphor were prepared by the dehydration of corresponding hydroxides Gd_1-x/2Eu_x/2(OH)₃ obtained by the hydrothermal reaction. Highly uniform nanowires of 20-30 nm in diameter can grow up to several tens of micrometers in length. A number of defects on the surface of Gd_1.92Eu_0.08O₃ nanowires, which are induced during structural transformation from hexagonal hydroxide to cubic oxide, strongly decrease the luminescence efficiency in comparison with that of the bulk phosphor. In contrast, the photoemission intensity of nanowires is significantly improved with increasing Eu³⁺ content (x) of Gd_2-xEu_xO₃ solid solution. The highest relative emission intensity of nanowires is observed when the x value is close to x=0.20. This content is much higher than the optimal concentration of Eu³⁺ (x=0.08-0.10) for the bulk Gd₂O₃:Eu powder.